All About polyester

Polyester resin sculpture in stone is synthetic and industrial work.

When drying polyester resin (Hardener) Mix and after a while its temperature increases.

And the gel is.

When I was stiff polyester molecules closer together and be part of the solution is steam.

And finally reduced amount of polyester after closing.

And other materials (Polyester is rigid) Can not be returned to a liquid state.

And best in class for working with polyester material Heat 20 is.

If more than five kilograms of liquid polyester daily consumption

Because it has a nasty smell ; This is done in a place that is well-ventilated area

And less than five kilograms per day in closed places is not harmful.

To prevent the polyester resin film should not cling to some objects such as wood or paraffin use.

What movie?

A liquid film on the mold surface is applied with a brush depilatory.

After being dried, a thin nylon layer is obtained.

Polyester resin storage conditions: Polyester resins should be kept in a cool dark place.

Expiration date for the exchange polyester resin :

Situations that are high qualities to twelve months (One year) Reaches.

When polyester closed and the other was hard and tough is not toxic.

File, navigate to drill the hole it.

Polyester resin does not change the light color.

And can be combined with color powder to be more colorful and stylish.

Dryers are (Hardener) Polyester is used for both liquid and pasty.

The dough easier to work with the type of liquid.

Liquid-liquid hardener nasty smell and color of water.

Hardener as polyester:

With low and high hardener can be difficult and hard time getting it set.

Typically normal amount of hardener in polyester resin that is transparent 2 Percent.

When a thin layer of polyester resin hardening time it goes slower.

And its upper part has a viscosity.

When this happens, the amount of hardener to 4 % Of our.

If the thickness of the layer of polyester is high probability of cracking is high

In this case, the amount of catalyst 1 Percent of the.

Also, when the plastic mold used because of the sensitivity of the film format, the hardener should be reduced.

When the amount of hardener 4 Pass percentage of polyester is allowed Brittle.

To be flexible and polyester are the catalyst should be one percent.

the catalyst :

Accelerator in polyester material in purple liquid, which compounds are.

The size of the accelerator while polyester is effectively closes.

Many accelerators to reduce setting time.

And makes polyester paint or red like dried vials Zero.

Article accelerator closing is effective in heat.

Preparation of Polyester with accelerator :

Initially the accelerator in polyester mix well we Myryzym.v.

After that we will add hardener material.

tip:

We should remember that any time the accelerator and hardener do not mix.

Because heat is generated and reacts.

And lead to a fire or explosion.

When the accelerator is greater when the action is faster polymerization produces more heat.

When polyester ties:

The amount of the hardener and the accelerator and polyester Close effective at room temperature.

As well as non-transparent polyester closing time longer than polyester that is transparent.

To build a statue of powder or paste paint color to paint the famous mother with polyester and blended and then we add cobalt.

After the conclusion of the statue of the outer mold when we have uniform color statue.

Polyester sculptures can be instant color for cars or colored ink .

Painting with ink and brush some ThINNER mixed with acetone polyester statue Mymalym.

Another color that is used for sculptures made of polyester, acrylic paint is.

Titanium powder and toothpaste to whiten the white polyester used.

And to make polyester to metal powder and powder metal corona can use.

For the polyester is less volume of materials such as carbon powder, calcium, chalk, talcum powder and wood can be used.

But of lime and plaster Avoid.

Pera oxide (dryer) Add at the end to tighten the time ahead.

To make a statue or hollow object must continually mold is rotated until the polyester gel. And for closing the mold a bit of polyester blended into the mold and it is our standing